What screw barrel is used for wire and cable extrusion?

Wire and cable insulation and sheathing are normally extruded on single screw barrels, sized to the conductor and line speed rather than to bulk output. The specification is driven by the compound: PVC, PE, XLPE, halogen-free LSZH and semiconductive layers each behave differently. EJS produces wire and cable extrusion screw barrels for construction, automotive, power and communication cable, in diameters from 12 mm to 500 mm.

Why do LSZH compounds wear screw barrels so quickly?

Halogen-free flame retardant compounds achieve their fire performance through very high loadings of mineral flame retardant fillers. Those mineral particles are abrasive, and the loading is far higher than in a typical filled compound, so they grind the flight lands and bore continuously. A nitrided case of 0.4 to 0.7 mm can be worn through relatively quickly, which is why bimetallic construction with a carbide-bearing alloy is the usual specification for LSZH duty.

Should a cable extrusion screw barrel be nitrided or bimetallic?

It depends on the compound. Clean unfilled polyethylene insulation runs well on a nitrided screw barrel. PVC is corrosive because it releases hydrogen chloride, LSZH is highly abrasive from mineral filler loading, and semiconductive compounds are loaded with conductive carbon black. Those three normally call for bimetallic construction, with the alloy chosen for whichever mechanism leads.

Why does melt uniformity matter more in cable extrusion?

Because a defect in cable is not cosmetic. An unmelted particle, a gel or a contaminant embedded in insulation creates a local weak point in the dielectric, and wall thickness variation means the insulation is thinner than design somewhere along the run. Both are electrical and safety issues rather than appearance issues, which is why mixing quality and consistent output are specified more tightly than in many other extrusion processes.

What causes wall thickness variation in cable insulation?

Unstable melt delivery is a common hardware cause. As the clearance between screw and barrel opens through wear, melt slips backward over the flights, output fluctuates and die pressure surges, and that variation transfers directly to insulation wall thickness at line speed. Measuring screw outer diameter and barrel bore against original dimensions will confirm whether wear is the source.

Do semiconductive cable compounds need a special screw barrel?

They need particular attention to both wear and cleanliness. Semiconductive layers are heavily loaded with conductive carbon black, which is abrasive, so bimetallic construction is common. Dispersion quality also matters because the layer must be electrically uniform, and any degraded or contaminated material carried through becomes a defect in a layer whose whole purpose is a smooth electrical interface.

What size cable extrusion screw barrels does EJS make?

EJS produces single screw extruder barrels from 12 mm to 500 mm diameter with working lengths up to 10,000 mm, covering wire and cable extrusion for construction, automotive, power and communication cable. Mixing elements including Maddock, Pineapple and Saxton designs can be built into the screw, and parts are made to drawing or to machine brand and model code.

Kable Estrusioa Torloju Barrilak: Konposatuak Dena erabakitzen du

EJS Talde Teknikoa· 2026ko abuztua · Eskaera gida

Estrusio gehienetan, gel bat edo urtu gabeko partikula bat kalitatezko kexa da. bateankable-estrusioa torloju-kanoia, hogeita hamar urtez horma edo hodi batean eseriko den dielektriko baten puntu ahula da. Ondorioz, ezberdintasun hori da zehaztapen osoa gidatzen duena.

Hariek eta kableek konposatu ezohiko zabala estaltzen dute: hardwarerako erraza den polietileno garbitik hasi eta jaten duten halogenorik gabeko formulazioetaraino. Prozesu-kategoria bera, lerro-diseinu bera, torlojuaren eta kanoiaren eskakizun oso desberdinak. Gida hau konposatuz doa, hori baita zure zehaztapena benetan erabakitzen duen aldagaia.

Single screw barrel for wire and cable extrusion produced by EJS

1. Zergatik epaitzen den kablearen estrusioaren torloju-kanoi bat modu ezberdinean

Hiru gauzek bereizten dute kable-lana estrusio orokorretik, eta hirurek maila igotzen dute urtze-kalitatearen errendimendua baino.

Akatsa elektrikoa da.Isolamenduan txertatuta dagoen kutsatzaile edo urtu gabeko partikula bat dielektrikoko eten lokal bat da. Ez da bezero batek ohartzen eta barkatzen duen zerbait; probetan edo okerrago, zerbitzuan agertzen den zerbait da.

Horma zehaztapen bat da, ez estetika.Isolamenduaren lodiera diseinatuta dago. Ibilbidean zehar aldatzeak esan nahi du kablea diseinua baino meheagoa dela nonbait, eta lodieraren aldakuntzak zuzenean itzultzen dira urtzeko entregaren egonkortasunera.

Lerroa azkar eta luze doa.Kable-lineak abiadura handian doaz denbora luzez, beraz, ezegonkortasuna konposatzen da eta higadura pilatzen da etenik gabeko ibilbide luzeetan.

Gainerakoan, urtu gabeko bat daerrefus kosmetikoa. Kableen isolamenduan, a dadielektrikoko puntu ahula.

2. Bost kable konposatu, bost zehaztapen desberdin

Hona hemen kable-material arruntek metalaren aurka nola jokatzen duten, leunenetik zigorgarrienera.

PE eta XLPE isolamendua

Nitruratua normalean ondo

Bete gabeko polietileno garbia estrusioa bezain ona da hardwarearekin, ez urratzailea ez korrosiboa. Hemen eskaria ez da higadura erresistentzia baizikurtu garbitasuna eta uniformetasuna, isolamendu-mailako PE zehazki horretan epaitzen delako.

Kalifikazio gurutzagarrietarako, tenperatura kontrolak modu zehatz batean du garrantzia: konposatuak kupelean aktibatu behar ez duen gurutzaketa-pakete bat darama. Gehiegizko zizaila-beroa ez da energia-kostua soilik, kiskaltzeko arriskua da.

Erasoak—Oso gutxi. Zehaztu urtze-kalitaterako eta zizaila kontrolatzeko, ez higadurarako.

PVCko isolamendua eta estaldura

Korrosioaren eraginez bimetalikoa

PVCa da alanbrea eraikitzeko eta erabilera orokorreko estalduraren zaldia, eta bere arazo ezaguna dakar: termikoki degradatzen den heinean askatzen da.hidrogeno kloruroa, lan-azalak korroditzen dituena. Kable PVCa ere plastifikatu egiten da eta normalean bete egiten da, gainean osagai urratzailea gehituz.

Aleazio aukerak korrosioarekiko erresistentzia izan behar du. EJS upel aleazioetan, norabidea adierazten dutenakEJS02 edo EJS03, Torlojuan Ni60 edo Colmonoy 56 gogorrekin.

Erasoak— korrosioa batez ere, urradura bigarrenik betegarritik.

LSZH / halogenorik gabeko suaren aurkakoa

Karburo-mailako bimetalikoa

Hau da jendea harritzen duen konposatua. Halogenorik gabeko konposatuek suaren errendimendua lortzen duteGarratze mineralaren karga oso handiak— betetako konposatu tipiko baten gainetik kargak. Partikula mineral horiek gogorrak dira, eta horietako asko daude.

0,4-0,7 mm-ko nitrurozko kasua ebakuntza batek PE esperientziatik espero duen denboraren zati batean eraman daiteke. Betebehar honek tungsteno-karburozko aleazio bat nahi du:Colmonoy 83torlojuan,EJS04zuloan.

Erasoak- urradura larria. Higadura gehien erabiltzen duen kable konposatua.

Geruza erdieroaleak

Bimetalikoa + sakabanaketa

Eroale eta isolamendu pantailak kargatuta daudekarbono beltza eroalea, hau da, urratzailea, eta geruzaren helburu osoa interfaze leuna eta elektrikoki uniformea aurkeztea da. Beraz, betebehar honek bi gauza eskatzen ditu aldi berean: higadura erresistentzia eta dispertsioaren kalitatea nahikoa ona den geruza elektrikoki koherentea izateko.

Konbinazio hori non anahasketa elementuaaleazio gogor batekin batera bere kostua irabazten du - aglomeratuak hausteko nahasketa barreiagarria, hemen aglomeratua akats elektriko bat baita.

Erasoak— karbono-beltzaren urradura, gehi dispertsio gogorraren baldintza.

Gomazko kable-jaka eta isolamendua

Makina ezberdina guztiz

Kautxuz jantzitako kablea ez da plastikozko kablearen estrusioaren aldaera bat; prozesu desberdina da hardware desberdinetan. Kautxua ez da urtzen; berotu, mozten eta nahasten du sendatzen utzi gabe. Kable-jaka goma normalean exekutatzen dapin upel hotzeko elikadura-estrusoreak, sarritan zuladura txikiagoa L/D luzeagoa duena, nahasketa guneek lan egiteko lekua izan dezaten.

Bimetalikoa estandarra da jaka konposatuak polimero kloratuak edo betegarri karga astunak daramatzanean. EJS-k Ø60–500 mm-ko pin torloju-upelak eta Ø60–650 mm-ko elikadura bero/hotza gomazko upelak eraikitzen ditu — guztiz estalita.gomazko torlojuaren gida.

Erasoak— konposatuaren araberakoa da; puntu handiena gomazko hardwarea behar duela da, ez plastikozko hardwarea.

3. Kable konposatuen hautaketa taula

Kable konposatua torloju-kanoiaren zehaztapena. Bi mekanismo daudenean, zenbat eta kaltegarriagoa den aleazio-aukera eramaten du.
Konposatua	Eraso nagusia	Gainazaleko tratamendua	Gomendatutako aleazioa
PE isolamendua (bete gabe)	Gutxienekoa	Nitruratua	—
XLPE	Gutxienekoa, kiskaltzeko arriskua	Nitruratua	—
PVC isolamendua / zorroa	Korrosioa + betegarria	Bimetalikoak	EJS02 / EJS03 · Ni60 edo Colmonoy 56
LSZH halogenorik gabekoa	Urradura handia	Bimetalikoak	EJS04 · Colmonoy 83
Erdieroalea	Urradura + sakabanaketa	Bimetalikoa + nahastea	EJS04 · Colmonoy 83
Gomazko jaka	Konposatuaren arabera aldatzen da	Nitruratuak edo bimetalikoak	Pin kanoi hardwarea

Industriaren ohar orokorra:goiko eraso-mekanismoek familia konposatu hauek estrusioan orokorrean nola jokatzen duten islatzen dute. Benetako kargak asko aldatzen dira formulazioen artean, beraz, berretsi betegarri mota eta ehunekoa zure konposatuan, kategoria-izena hartu beharrean.

4. Kableen akatsak Hardwarera itzultzea

Kable-arazo guztiak ez dira torloju-arazo bat, baina hainbat dira, eta merezi dute hasieran ezagutzea, zehaztapenik gabe geratzen den kable-lerro bat bobinagatik garestia delako.

Kablearen estrusioaren ohiko sintoma hardware kausa batekin.
Ikusten duzuna	Litekeena da hardwarearen kausa	Nola egiaztatu
Hormaren lodiera ibilbidean zehar aldatzen da	Urtze banaketa ezegonkorra; sakea irekita	Neurtu torlojuaren OD eta kanoi-zuloa eta jatorrizkoa
Gelak edo urtu gabeko isolamenduan	Urtze edo nahasketa nahikoa ez	Berrikusi nahaste-atala eta torlojuaren geometria
Puntuak edo marra koloregabeak	Degradazioa puntu hiletan	Emariaren bidea eta punta arintzea ikuskatu
Irteera torlojuaren abiadura berean erortzen da	Higadura — urtu hegaldien gainean irristatzea	Oinarrizko lerroaren dimentsio-kontrola
Urtze-tenperatura igotzen da, ezarpen berdinak	Sakea irekita, zizaila gehigarria	Dimentsio-kontrola
Erdiko geruzaren erresistentzia irregularra	Karbono beltzaren sakabanaketa eskasa	Berrikusi nahaste dispertsiboaren atala

LSZH lerroetan ikustea merezi duen eredua:PVCtik edo PEtik halogenorik gabeko konposatuetara aldatzen diren eragiketek ordezkapen-tarte bera mantentzen dute maiz mantentze-planean. Konposatua aldatu egin zen; higadura-tasa aldatu egin zen horrekin. Gainazaleko tratamendua ere aldatu ez bada, multzoa bere bizitza erabilgarriaren amaierara egutegiak espero baino askoz lehenago iritsiko da.

5. Lerroaren abiadura, urtze-egonkortasuna eta zergatik higadura agertzen da hemen lehenik

Kablearen isolamendua abiaduran mugitzen den eroale bati aplikatzen zaio. Horrek esan nahi du estrusoreak ez duela materiala soilik entregatzen, baizik eta entregatzen ari delalineako abiadurarekin sinkronizatuta dagoen abiadura etengabean— eta edozein gorabehera horma-mikran neurtutako produktu baten dimentsio-aldaera bihurtzen da.

Horregatik, sakearen higadura kablearen kalitatean prozesu gehienek nabarituko luketena baino lehenago agertzen da. Torlojutik kanoirako tartea irekitzen den heinean, urtzea atzerantz irrist egiten da hegaldien gainean, aurrera eraman beharrean. Irteera noraezean doa, trokelaren presioa egonkorrago bihurtzen da eta hormaren lodiera jarraitzen du. Inork torlojuari "higatuta" deitu baino askoz lehenago, lineak zehaztapenetan jarraitzeko tolerantzia-kudeaketa estuagoa behar duen kablea sortzen ari da.

PTA hardfacing on screw flights for abrasive cable compounds — PTA hardfacing - LSZH eta betegarri erdieroaleen kargaren erantzuna

Mixing element for dispersion in cable compounds — Nahasketa-elementua — dispertsioaren kalitatea erdiko geruzetako propietate elektrikoa da

Erantzun praktikoa da berrien oinarri neurtua edukitzea eta aldian-aldian egiaztatzea, atalean ezarritakoaren araberazure torloju-kanoia gastatuta dagoela adierazten du. Kable-lerro batean itzulera ez da bizitza zati bat bakarrik; kalitatearen noraeza hardwarearen azalpena noiz duen jakitea da.

6. Alanbre eta kable estrusiozko torloju-kanoia zehaztea

EJS-k alanbre- eta kable-estrusio-torloju-upelak ekoizten ditu eraikuntza, automobilgintza, elektrizitate-kable eta komunikazio-hari industrietarako. Torloju bakarreko upeletatik irteten dira12 mm eta 500 mm arteko diametroalan luzerarekin10.000 mm, eraikuntza nitruratua edo bimetalikoan, Maddock, Pineapple eta Saxton nahasketa-elementuak eskuragarri eta elikadura-etxe, elikadura-estalkia eta ur-jaka barnean ekoiztuta.

Kable torloju-kanoiaren kontsultan zer adierazi

Konposatua izenaren eta betegarrien kargaren arabera— "LSZH" eta "PVC zorroak" aleazio desberdinak sortzen dituzte; betegarri-portzentajeak gehiago fintzen du
Zein geruza— pantaila eroalea, isolamendua, isolamendu pantaila, ohea, zorroa
Makinaren marka, modeloa eta torlojuaren diametroa, gehi L/D ezagutzen bada
Linearen abiadura eta irteera-helburua
Egungo edozein akats— hormaren aldakuntza, gelak, motak, erresistentzia arazoak
Marrazkiaeskuragarri badago; bestela argazkiak gehi diametroa, luzera eta brida xehetasunak

Ordezko lanetan ez da marrazketa normala - gure ingeniariek lehendik dagoen torloju-kanoi bat neur dezakete gunean, makinaren marka edozein dela ere. Piezak Ra 0,4 µm gainazaleko zimurtasunarekin eta 0,015 mm-ko zuzentasunarekin eraikitzen dira, eta materialaren ziurtagiriarekin eta ikuskapen-txostenarekin bidaltzen dira. Eskaintzak normalean lanegun bateko epean ematen dira informazioa argi dagoenean.

Egiten ditugun galderak

Zein torloju upel erabiltzen da alanbre eta kable estrusiorako?

Hariaren eta kableen isolamendua eta estaldura normalean torloju bakarreko upeletan estruitzen dira, eroalearen eta linearen abiaduraren neurrian, irteera handirako baino. Zehaztapena konposatuak gidatzen du: PVC, PE, XLPE, halogenorik gabeko LSZH eta geruza erdieroaleek portaera ezberdina dute. EJS-k eraikuntzarako, automoziorako, potentziarako eta komunikaziorako kableetarako alanbre eta kable estrusiorako torloju kableak ekoizten ditu, 12 mm-tik 500 mm-ra arteko diametroetan.

Zergatik janzten dituzte LSZH konposatuek hain azkar torloju-upelak?

Halogenorik gabeko suaren aurkako konposatuek suaren errendimendua lortzen dute suaren erresistentearen betegarri mineralen karga oso handien bidez. Partikula mineral horiek urratzaileak dira, eta karga betetako ohiko konposatu batean baino askoz ere handiagoa da, beraz, hegaldia lurzoruan ehotzen dute eta etengabe zulatzen dute. 0,4 eta 0,7 mm-ko nitrurozko kaxa nahiko azkar gastatu daiteke, horregatik karburodun aleazio batekin eraikuntza bimetalikoa da LSZH funtziorako ohiko zehaztapena.

Kablearen estrusiozko torloju-kanoi bat nitruratua edo bimetalikoa izan behar al da?

Konposatuaren araberakoa da. Bete gabeko polietilenozko isolamendu garbia ondo doa nitruratuzko torloju-upel batean. PVC korrosiboa da hidrogeno kloruroa askatzen duelako, LSZH oso urratzailea da mineralen betegarrien kargagatik eta konposatu erdieroaleak karbono beltzez kargatuta daude. Hiru horiek normalean eraikuntza bimetalikoa eskatzen dute, edozein mekanismotarako aukeratutako aleazioarekin.

Zergatik du garrantzi handiagoa kablearen estrusioan urtze-uniformitateak?

Kablearen akats bat ez baita kosmetikoa. Isolamenduan txertatutako partikula urtu gabeko, gel edo kutsatzaile batek tokiko puntu ahul bat sortzen du dielektrikoan, eta hormaren lodieraren aldakuntzak esan nahi du isolamendua diseinua baino meheagoa dela ibilbidean zehar. Biak elektriko eta segurtasun-arazoak dira itxura-arazoak baino, horregatik kalitatea eta irteera koherentea nahastea beste estrusio-prozesu askotan baino estuago zehazten da.

Zerk eragiten du hormaren lodieraren aldakuntza kableen isolamenduan?

Urtze ezegonkorra hardwarearen kausa ohikoa da. Torlojuaren eta kanoiaren arteko sakea higaduraren ondorioz irekitzen den heinean, urtzea atzerantz irrist egiten da hegaldien gainean, irteerak gora egiten du eta trokelaren presioa igotzen da, eta aldakuntza hori isolamendu-hormaren lodiera zuzenean transferitzen da lineako abiaduran. Torlojuaren kanpoko diametroa eta kanoi-zuloa jatorrizko dimentsioen arabera neurtzeak higadura den iturria dela baieztatuko du.

Kable erdieroaleen konposatuek torloju-kanoi berezi bat behar al dute?

Arreta berezia behar dute bai higadurari bai garbitasunari. Geruza erdieroaleak karbono beltzez eroalez kargatuta daude, hau da, urratzailea, beraz, eraikuntza bimetalikoa ohikoa da. Dispertsioaren kalitateak ere garrantzia du geruzak elektrikoki uniformea izan behar duelako, eta hondatutako edo kutsatutako edozein material interfaze elektriko leuna den geruza baten akats bihurtzen baita.

Zein tamainako kable estrusio torloju-upelak egiten ditu EJS-k?

EJS-k 12 mm-tik 500 mm arteko diametroa duten torloju-estrusio-upel bakarrak ekoizten ditu 10.000 mm-ko luzerarekin, eraikuntzarako, automoziorako, potentziarako eta komunikaziorako kableetarako alanbre eta kable estrusioa estaltzeko. Maddock, Pineapple eta Saxton diseinuak barne nahasteko elementuak txerta daitezke torlojuan, eta piezak marrazteko edo makinaren marka eta modelo kodearekin egiten dira.